Wide-bandgap oxide semiconductors have received significant attention as they can produce devices with high output and breakdown voltage. p-Type conductivity control is essential to realize bipolar devices. Therefore, as a rare wide-bandgap p-type oxide semiconductor, NiO (3.7 eV) has garnered considerable attention. In view of the heterojunction device with Ga2O3 (4.5–5.0 eV), a p-type material with a large bandgap is desired. Herein, we report the growth of a Ni1-xMgxO thin film, which has a larger bandgap than NiO, on α-Al2O3 (0001) substrates that was developed using the mist chemical vapor deposition method. The Ni1-xMgxO thin films epitaxially grown on α-Al2O3 substrates showed crystallographic orientation relationships identical to those of NiO thin films. The Mg composition of Ni1-xMgxO was easily controlled by the Mg concentration of the precursor solution. The Ni1-xMgxO thin film with a higher Mg composition had a larger bandgap, and the bandgap reached 3.9 eV with a Ni1-xMgxO thin film with x = 0.28. In contrast to an undoped Ni1-xMgxO thin film showing insulating properties, the Li-doped Ni1-xMgxO thin film had resistivities of 101–105 Ω∙cm depending on the Li precursor concentration, suggesting that Li effectively acts as an acceptor.

Alkali-borosilicate glasses (ABS) are used as host immobilization matrices for different radioactive waste streams and are characterized by their ability to incorporate a wide variety of metal oxides with respectively high waste loadings. The vitreous wasteform is also characterized by very good physical and chemical durability. The durability of three ABS compositions were analyzed by investigating their leaching behavior using the MCC1 test protocol and these data were used to investigate the waste components retention in the altered layer and the evolution of the interfacial water composition during the test. The results indicated that the Mg species evolution is exceptional with respect to other alkaline elements and dependent on glass matrix composition and leaching progress, while transition elements speciation is fairly constant throughout leaching process and independent on glass compositions. Si and B species are changing during leaching process and are affected by waste composition. For modified wasteform sample, evolution of Mg, Si and B species is respectively constant, whereas at highest waste loading, these elements have fairly constant speciation evolution within the first 2 weeks of leaching.

We report a facile method to fabricate CuNi nano-octahedra and nanocubes using a colloidal synthesis approach. The CuNi nanocrystals terminated with exclusive crystallographic facets were controlled and achieved by a group of synergetic capping ligands in a hot solution system. Specifically, the growth of {111}-bounded CuNi nano-octahedra is derived by a thermodynamic control, whereas the generation of {100}-terminated CuNi nanocubes is steered by a kinetic capping of chloride. Using a reduction of 4-nitrophenol with sodium borohydride as a model reaction, CuNi nano-octahedra and nanocubes demonstrated a strong facet-dependence due to their different surface energies although both exhibited remarkable catalytic activity with the high rate constant over mass (k/m). A kinetic study indicated that this is a pseudo first-order reaction with an excess of sodium borohydride. CuNi nanocubes as the catalysts showed better catalytic performance (k/m = 385 s-1•g-1) than the CuNi nano-octahedra (k/m = 120 s-1•g-1), indicating that 4-nitrophenol and hydrogen were adsorbed on the {100} facets with their molecules parallel to the surface much easier than those on {111} facets.

The purpose of this work was the synthesis of the perovskites with rare earth, by gel combustion method with pigmenting, magnetic and luminescent properties. The synthesis of perovskite structure is important for material development, with multi features. In this work, the synthesis was from metal oxides by the method of combustion of gels at 500 °C, for 10 s. Color of perovskites obtained, with nanometric particle size (31-44 nm) was analysed by CIEL*a*b* with tonalities ranged from white to pink except for Pr-perovskites with yellow and brown. Its paramagnetic properties were verified by magnetic susceptibility. Its luminescence was at 260 nm, except for Pr-perovskites. This work opens an important opportunity to develop ceramic pigments with perovskites structures integrating other properties as luminescence and paramagnetism by combustion sol-gel method.

Phase change materials (PCMs) are getting increasing interest due to their capacity to absorb, store and release heat energy. Their effectiveness is characterized by quantities of absorbed/released heat energy, expressed as enthalpy. Specifically, the larger is the enthalpy, the more efficient thermoregulation effect is achieved. With this in mind, PCMs can be used in the manufacture of thermally regulated clothing in order to minimize heat strain and simultaneously improve thermal comfort. Moreover, such materials also modify their infrared radiation emission during phase transition, thus they can be envisioned to exploit thermal shielding applications. The aim of the present research was to investigate the infrared emissivity of textiles composed by cotton yarns with dispersed PCMs. The organic microcapsules of phase change materials, having different binding to the fibre mechanisms, were padded onto the fabric surface by pad-dry-cure method. The thermal properties and stabilities were measured using differential scanning calorimetry, while infrared emissivity was characterized using infrared thermographic technique. The obtained experimental results show a dynamic tuning of IR emissivity during heating/cooling process which can be correlated to the type and properties (enthalpy of fusion) of the corresponding PCM.

Enzymes can be a renewable source of catalytic agents and thus be interesting for sustainable approaches to create and modify functional materials. Here, thin hydrogel layers were prepared as thin coatings on hard substrates by immobilized horseradish peroxidase. Hydrophilic 4-arm star shaped telechelics from oligo(ethylene glycol) bearing on average 55% end groups derived from aromatic amino acids served as monomers and enzymatic substrates. Shifts of the contact angle from 84° to 62° for the wetting process and of zeta potential towards the neutral range illustrated an alteration of physicochemical properties of the model surfaces by a hydrophilic shielding. Time-of-flight secondary ion mass spectrometry (ToF-SIMS), quartz crystal microbalance and atomic force microscopy (AFM) experiments enabled the qualitative and quantitative proof of hydrogel deposition at the interface with thicknesses in the medium nanometer size range. Conceptually, as the immobilized enzyme becomes entrapped in the hydrogel and the crosslinking mechanism bases on a radical reaction after enzymatic activation of the monomers with a limited diffusivity and lifetime, the formed network material can be assumed to be inhomogeneous on the molecular level. On the macroscale, however, relative homogeneity of the coating was observed via ToF-SIMS and AFM mapping. As an exemplary functional evaluation in view of bioanalytical applications, the thrombogenicity of the coating was studied in static tests with human blood from several donors. In the future, this “coating-from” approach may be explored for cell culture substrate coatings, for protein/biofilm repellence in technical applications, or in bioanalytical devices.

Burnups can cause major structural changes in the edge of the fuel rod and a general degradation of the thermal conductivity. In irradiated mixed oxide fuels of UO2, PuO2 with NpO2 as fission products (FP) various chemical states depending on the conditions of the fuel is developed. This work, we firstly applied the MD relation to obtain the thermal conductivity of UO2, PuO2, and (U, Pu) O2 in temperature range of 300–2000 K. Lattice parameter, Burnup and the thermal conductivity were then calculated for specified UO2 and PuO2. This calculation relates the degradation of thermal conductivity with a number of pores and increasing temperature. Finally, the migration energy barrier and the recovery energies of the obstruction type defects were calculated with molecular dynamics simulation.