Twelve nontronites and two ferruginous smectites have been characterized with respect to Fe3+ occupancy of tetrahedral sites. The techniques used were near infrared, Fe-K X-ray absorption near-edge and X-ray absorption fine-structure spectroscopies, along with two X-ray diffraction techniques. The results show that calculations of the structural formulae of many nontronites should be adjusted to include Fe3+ in tetrahedral sites. The nontronite from Spokane County, Washington, (∼44% Fe2O3) is essentially an end-member with its non-siliceous tetrahedral sites occupied by Fe3+. Samples with chemical compositions similar to Garfield nontronite (∼36.5% Fe2O3) may have small amounts (<5% of total Fe3+) of tetrahedral Fe3+. Tetrahedral Fe3+ is unlikely to be present in samples containing less than ∼34% Fe2O3.

Details of the quantitative techniques successfully applied to artificial rock mixtures distributed for the third Clay Minerals Society Reynolds Cup (RC) contest are presented. Participants each received three samples, two containing 17 minerals each and a third containing ten minerals. The true composition of the samples was unknown to all participants during the contest period. The results submitted were ranked by summing the deviations from the actual compositions (bias). The top three finishers used mainly X-ray diffraction (XRD) for identification and quantification. The winner obtained an average bias of 11.3% per sample by using an internal standard and modified single-line reference intensity ratio (RIR) method based on pure mineral standards. Full-pattern fitting by genetic algorithm was used to measure the integrated intensity of the diagnostic single-line reflections chosen for quantification. Elemental-composition optimization was used separately to constrain phase concentrations that were uncertain because the reference mineral standards were lacking or not ideal. Cation exchange capacity, oriented-sample XRD analysis, and thermogravimetric analysis were also used as supplementary techniques. The second-place finisher obtained an average bias of 13.9%, also by using an RIR method, but without an added internal standard and with intensity measured by whole-pattern fitting. The third-place finisher, who obtained an average bias of 15.3%, used the Rietveld method for quantification and identification of minor phases (using difference plots). This participant also used scanning electron microscopy (with X-ray microanalysis) to identify minor components and verify the composition of structures used in Rietveld analysis. As in the previous contests, successful quantification appears to be more dependent on analyst experience than on the analytical technique or software used.

Thirty two boehmites, synthesized at temperatures ranging from room temperature to 300°C, were examined by scanning electron microscopy, transmission electron microscopy, electron diffraction, X-ray powder diffraction, differential thermal analysis, and infrared spectroscopy. The results show that boehmite exhibits a continuous gradation in crystallite size ranging from single octahedral layers or a few unit cells to about 65 unit cells in the y-direction. This conclusion suggests that the term pseudoboehmite is inappropriate for finely crystalline boehmite. Finely crystalline boehmite contains more sorbed water than coarsely crystalline boehmite; this water is commonly intercalated between octahedral layers, usually randomly but sometimes regularly. The regularly interstratified boehmite gives rise to a diffuse “long spacing” X-ray diffraction reflection. Calculated 020 X-ray diffraction peaks approximate closely those observed experimentally when a range of crystallite sizes is taken into account.

Specific surface area measurements of The Clay Minerals Society source clays were made by the Brunauer, Emmett and Teller (BET) method of adsorption of nitrogen gas. Two replicate measurements of specific surface area were performed for each source clay. All pair values were within 3%, which is very good agreement for this type of measurement.

The broad charge heterogeneity typical of nearly all smectites is not necessarily characteristic of vermiculites. In addition to vermiculites with pronounced heterogeneity, minerals with no or only limited charge heterogeneities are known. Layer charge and charge heterogeneity of 25 vermiculites were determined by alkylammonium ion exchange. The comparison of experimental basal spacings with dL/n-plots provided a simple determination of the average charge density. The spacings of high-charged vermiculites (≥0.8 eq/(Si,Al)4O10) with paraffin-type interlayers follow a straight line in the dL/n-plots. Lower-charged vermiculites were recognized by stepwise increasing spacings due to mono-, two-, or three-layer chain packings. Charge heterogeneity produced a superposition of the dL/n-curves for different charges, and the basal reflections of some of the alkylammonium derivatives became nonintegral.

Interlayering of 2: 1 layer silicates varies as a function of chemical weathering from the simple, homogeneous K or Na interlayers of micas to the heterogeneous systems of mica intercalated with expanded 2: 1 layer silicates. “Frayed edge” type of weathering at dislocation planes of mica is collated with K release and preferential cation-exchange uptake of K relative to Ca by such expansible layer silicate systems; mica islands maintain alignment of the silica sheet cavities, which facilitates recapture of lattice K. Intercalation of the expanded 2: 1 layer silicates with alumina interlayers appears to be a characteristic function of chemical weathering in soils, with the formation of 2: 1–2: 2 intergrades not only of 14 Å spacing but also of swelling 18 Å types that give small 12, 14, 18 Å and higher spacing peaks (along with the 10 Å peak) at 550°C. Interlayer precipitates appear to be characteristic of soil clays, contrasting with “pure” minerals of deposits developed in less “open” environments than those of soils. The “2: 2 lattice building” phenomenon in expansible 2: 1 layer silicates relates to layer charge density and crystal size, and frequently tends to inhibit the formation of free gibbsite in soil chemical weathering so long as there are expansible layer silicates present to become intercalated with aluminum hydroxide—a weathering phenomenon that may be called an “antigibbsite effect”. Accumulation of alumina (possibly with some iron, magnesium, and allophane) as interlayers in 2: 1 minerals of soils is seen as a genetic stage in the 2: 2 → 1: 1 weathering sequence through which kaolinite and halloysite develop in soils.

A layered double hydroxide with a chemical composition [Al2Li(OH)6]+X− · nH2O, where X− is an interlayer anion, has been synthesized hydrothermally at 130°C from aluminum-tri-(sec-butoxide) and lithium carbonate. Electron micrographs showed the product to have a platy morphology with distinct hexagonal symmetry, which has been corroborated by selected area electron diffraction patterns corresponding to a projection of the structure on its (001) plane. Evidence for a superlattice with a = 5.32 Å was obtained, indicating cation ordering among octahedral sites. X-ray powder diffraction data also can be interpreted by reference to a hexagonal supercell with dimensions a = 5.32 Å and c = 15.24 Å. The arrangement of the octahedral sites appears to be that of gibbsite, but with the vacancies filled with lithium cations. Anions must be present between the sheets to balance the charge. A complete assignment of the observed infrared lattice vibrations can be made for the anion [Al2LiO6] with the ideal D3d symmetry for motions within one octahedral sheet. The results show that [Al2Li(OH)6]+X− · nH2O is a hydrotalcite-like compound with the octahedral cations largely ordered. The general formula for hydrotalcite-like compounds, [M2+1−xM3+x(OH)2]x+Xm−x/m · nH2O, should be extended to include the monovalent lithium cation.

The adsorption of sodium, chloride, and phosphate ions by allophane, imogolite, and halloysite has been studied in relation to the surface structure of the mineral samples. The high adsorption of phosphate (>200 μmole/g) and chloride (10–30 meq/100 g at pH 4) by allophane is ascribed to the small particle size of allophane, its high surface area (∼800 m2/g), and the presence at the surface of Al-OH-Al groups and defect sites. In contrast, halloysite has a relatively large particle size and a Si-O-Si surface. Accordingly, the adsorption of phosphate (5–10 μmole/g) and chloride (1 meq/100 g) by halloysite is very much lower as compared with allophane. Phosphate adsorption by halloysite is also related to particle morphology and the number of edge sites. Thus, a sample consisting entirely of spheroidal particles adsorbed only 5 μmole/g at a solution concentration of 1 × 10−4 M, whereas the tubular types of comparable surface area adsorbed 7–10 μmole/g at the same concentration. This is because spheroidal halloysite particles have few, if any, edge sites at which phosphate can adsorb. The relative degree of order and hydration of halloysite, as indicated by infrared spectroscopy, also affects phosphate adsorption. However, this factor is apparently less important than particle morphology and surface structure. Although imogolite also has an Al-OH-Al surface, it contains relatively few defect sites where phosphate can adsorb. Consequently, much less phosphate (120 μmole/g) was adsorbed as compared with allophane.

Thermal analysis involves a dynamic phenomenological approach to the study of materials by observing the response of these materials to a change in temperature. This approach differs fundamentally from static methods of analysis, such as structural or chemical analyses, which rely on direct observations of a basic property of material (e.g. crystal structure or chemical composition) at a well-defined set of conditions (e.g. temperature, pressure, humidity). Clay minerals are highly susceptible to significant compositional changes in response to subtle changes in conditions. For example, changes in the fugacity of water affect the stability of interlayer H2O in a clay mineral (see below). Therefore, care must be taken that all experimental conditions are known with accuracy and precision

Samples of Na-saturated, Upton montmorillonite were prepared with different contents of water (H2O or D2O) by: (1) adsorption of water from the vapor phase at a specific value of p/p°, the relative humidity, (2) adsorption of water from the vapor phase at p/p° = 1.0 followed by desorption of the water into the vapor phase at a specific p/p° < 1.0, and (3) adsorption of water from the liquid phase followed by desorption of the water into the vapor phase at a specific p/p° < 1.0. Water adsorbed initially from the vapor phase was called V-adsorbed water, and water adsorbed initially from the liquid phase was called L-adsorbed water. The water contents of these samples were determined by gravimetric analysis, the c-axis spacings by X-ray powder diffraction, the O-D stretching frequencies by IR spectroscopy, and the heats of immersion by differential microcalorimetry. No difference was found between V-adsorbed and L-adsorbed water; however, if the final water content was established by adsorption, the system was in a different state than if the final water content was established by desorption. In particular, hysteresis was observed in the following properties: the relative humidity of the adsorbed water, the O-D stretching frequency in this water, and the degree of order in the stacking of the clay layers. The only property that did not exhibit hysteresis was the heat of immersion. Apparently, hysteresis occurred because the orderliness of the system was not reversible, and, thus, any property that depended on orderliness was hysteretic.

Crystal growth theory was applied to describe edge sites of phyllosilicates. Three face configurations were found to exist. One face has one tetrahedral site per tetrahedral sheet and two octahedral one-coordinated sites per crystallographic area ac sin β, where a and c are layer dimensions and β is the angle between them. The other two faces are similar except that they have one less octahedral site which is replaced by one SiIV-O-AlVI site in this same ac sin β area. A transfer of bonding energy from the remaining octahedral site to the SiIV-O-AlVI site is believed to neutralize all edge charge on faces containing these latter sites at normally encountered pHs (pH 3–9). A similar charge rearrangement along the edges results in an apparent decrease in the permanent charge of the mineral with an increase in edge area.

On the basis of such an analysis, lath-shaped illite can be described as a very fine grained dioctahedral mica in which the apparent deficient occupancy of the octahedral sheet, presence of excess water, and measurable cation-exchange capacity may in part be the result of a large ratio of edge area to total volume, with no other chemical or structural change in the mica layers. The increasing importance of edge charge relative to layer charge produces erroneous formulae for 2:1 phyllosilicates in very fine grained samples containing fewer than 2 of 3 octahedral sites occupied by cations, on the basis of a 22-charge half cell.

Bentonite, biotite, illite, kaolin, vermiculite and zeolite were acidified or alkalized with hydrochloric acid or sodium hydroxide at concentrations of 0.1, 1.0 and 5.0 mole dm−3 at room temperature for two weeks. In acid treatments, dissolution of Al prevailed over Si and the opposite was observed in alkali treatments. The XRD patterns showed severe alteration of the crystal structure after acid treatments, whereas sharpening of the XRD peaks after alkali treatments was observed. Illite and kaolin were most resistant to acid attack. with a few exceptions, the surface areas of the minerals computed from both water and nitrogen adsorption isotherms increased with acid and alkali treatments. with increasing reagent concentration, the nitrogen surface area increased faster than the water surface area. well-defined trends were not noted in either changes of average water or nitrogen adsorption energies or in relative amounts of adsorption sites, indicating that the effects of acid and alkali attack are controlled by the individual character of the minerals.

Boron adsorption by Ca forms of montmorillonite, illite, and kaolinite was determined as a function of pH and boron concentration in solution. Data from batch experiments were compared with results computed for each clay according to fitted adsorption coefficients (maximum boron adsorption and affinity constants related to the binding energy). The agreement between calculated values and experimental results indicates that a phenomenological equation can be used to predict boron adsorption on clays as a function of both of these variables. For the solution-to-clay ratios examined, the water content does not affect the boron-surface interaction as expressed by the above adsorption parameters. Because the affinity of clays for B(OH)4− is much stronger than for B(OH)3 , the adsorption maximum was obtained only under alkaline conditions at approximately pH 9.0 to 9.7. It is suggested that the pH of maximum adsorption is a function of the ratios of affinity coefficients of the three species B(OH)3, B(OH)4−, and OH− competing for the same adsorption sites. The adsorption coefficients indicate that in some cases the difference in the amount of adsorbed boron between montmorillonite and kaolinite could be either small or large, depending on the circumstances. The main factor that would affect this difference is the total amount of boron in the suspension. Estimated value of the adsorption maximum was 2.94, 11.8 and 15.1 µmole/g for Ca-kaolinite, Ca-montmorillonite, and Ca-illite, respectively.

The structural formula of Kozfikov saponite (Czechoslovakia) is as follows:

$N{a_{0.005}}C{a_{0.22}}{K_{0.01}}[S{i_{3.30}}A{l_{0.68}}F{e^{3 + }}{}_{0.02}][M{g_{2.50}}F{e^{2 + }}{}_{0.26}F{e^{3 + }}{}_{0.24}]{O_{10}}{(OH)_2}.$

Historically, the decarbonation of Mg-Al-CO3 hydrotalcite-like compounds (HTlc) has been thought to occur between 400° and 500°C. The present work demonstrates that when HTlcs having the maximum Al content, Al/(Al + Mg) = 0.33, are heated to 500°C, 20–30% of the carbonates remain. The evolution of the remaining carbonates was observed as two maxima, at 600 and 900°C At these temperatures, Al ions go into MgO, and spinel (MgAl2O4) forms. Therefore, the carbonates are released as the Al ions migrate.

At a lower Al content, Al/(Al + Mg) = 0.25, CO2 evolution is almost complete at 500°C. This HTlc has no maximum of CO2 evolution above 500°C. Lower charge densities, due to lower Al contents, lead to lower amounts of remaining carbonate anions.

The vibrational modes of clay minerals are uniquely accessible to FT Raman spectroscopy, but this potentially powerful technique has found limited application to the study of clay mineral structure. Raman spectra in the 50 to 3800 cm−1 region were obtained for a number of kandite clays. The kandite clay minerals are characterised by relatively intense bands centred at 142.7 cm−1 for kaolinite, 143 cm−1 for halloysite and 131.2 cm−1 for dickite with prominent shoulders at 129, 127, and 120 cm−1 respectively. These vibrational modes are attributed to the O-Al-O and O-Si-O symmetric bends. Differences in the lattice modes for the kandite clay minerals in the 200 to 1200 cm−1 were obtained. Four OH bands were obtained for kaolinite 3621, 3652, 3668, and 3695 cm−1; three OH bands were found for a selection of dickites and halloysites. The San Juan Dickite and the Eureka Halloysite show further resolution of the low frequency 3620 cm−1 hydroxyl band. This splitting is attributed to variation in the position of the inner hydroxyls. Variation in band intensity and position was found to be sample dependent.

The effect of pH on the flocculation-dispersion behavior of noncrystalline aluminum and iron oxides, kaolinite, montmorillonite, and various mixtures of these materials was investigated. The clays were Na- or Ca-saturated and freeze-dried before use. Critical coagulation concentrations (CCC) of all materials and mixtures were found to be pH dependent. The Al oxide was flocculated at pH >9.5 and the iron oxide was flocculated between pH 6.0 and 8.2; i.e., flocculation occurred at pHs near the point of zero charge (PZC). The CCC of both the Na- and Ca-clay systems increased with increasing pH. The effect of pH was greater for the Na-kaolinite (flocculated at pH 5.8 and having a CCC of 55 meq/liter at pH 9.1) than the Na-montmorillonite system (having a CCC of 14 meq/liter at pH 6.4 and a CCC of 28 meq/liter at pH 9.4). A 50/50 mixture of Na-kaolinite and Na-montmorillonite behaved more like montmorillonite (having CCCs of 13 and 33 meq/liter at pH 6.2 and pH 9.0, respectively). The presence of either noncrystalline oxide decreased the CCC over that of the clay(s) alone; the decrease occurred at pHs >7 for Al oxide and at pHs >6.5 for Fe oxide. Aluminum oxide produced a greater decrease in CCC than Fe oxide, especially at pHs >8. The effect of each oxide on CCC was greatest near the PZC, 9.5 and 7.2 for Al and Fe oxide, respectively.

Three sepiolite clays studied showed evidence for the presence of structural hydroxyl groups in three to five different environments depending on the composition of the clay. A 3720 cm−1 i.r. frequency is shown to be characteristic of SiOH at crystal edges which are very abundant in sepiolites. This band has not been seen by most workers because the Nujol, fluorolube or KBr used in sample preparation perturb it sufficiently to obscure it under other OH stretching bands. The 3680 cm−1 band is confirmed as being from the (Mg)3OH and evidence of a very small band near 3640 cm−1 is suggested to arise from limited trioctahedral substitution. The very crystalline Ampandrandava sepiolite shows only the above three bands. The intermediately crystalline Vallecas shows a 3620 cm−1 band in addition which is characteristic of dioctahedral systems and is due to either some vacancy sites or to the presence of attapulgite. This dioctahedral band is greater in the less crystalline Salinelles sepiolite; in addition, it has a smaller 3585 cm−1 band. Mg-Al-vacancy and Mg-Fe‴-vacancy are suggested as the source of the 3620 cm−1 and 3585 cm−1 bands.